Model NO.
1001-1
Reflective Material Type
Reflective Fabric
Material
90/10 T/C
Application
Sewing on The Protective Safety Uniforms
Color
Silver
Certificate
En20471 & ANSI/Isea 107
Retroreflection
400cdl
Domestic Wash
>30circles@60 Degrees ( ISO6330:2A )
Wash Temperature
40 Degrees Best
Dry Clean
>5circles ( ISO 3175 )
Width
2.5cm/5cm/50cm/100cm,Other Size Upon Request
Trademark
HIGHVIZ
Transport Package
100m/Roll, Other Packing Upon Request
Specification
EN20471 Class 2 & ANSI/ISEA 107: 2010 Class 2
Origin
China
HS Code
5907009040
1001-1: Silver Reflective Tape,90/10 T/C Backing
1001-1 Reflective Tape is widely used for reflective safety clothing, professional uniforms, casual wear, sportswear, fashion clothing, hats, gloves, backpacks and personal protective equipment, etc., it can also be made into all kinds of reflective products,such as reflective armbands,reflective key rings,reflective signs,reflective stickers,reflective toys.
Retro-reflection Performance:
Initial coefficient of retro-reflection performance in cd/(lx )
1001-1 Reflective Tape is widely used for reflective safety clothing, professional uniforms, casual wear, sportswear, fashion clothing, hats, gloves, backpacks and personal protective equipment, etc., it can also be made into all kinds of reflective products,such as reflective armbands,reflective key rings,reflective signs,reflective stickers,reflective toys.
Retro-reflection Performance:
Initial coefficient of retro-reflection performance in cd/(lx )
| 1001-1: Silver Reflective Tape, T/C Base | ||||||||
| Observation Angle | Entrance Angle | |||||||
| 5° | 20° | 30° | 40° | |||||
| Test | Standard | Test | Standard | Test | Standard | Test | Standard | |
| 0.2° | 520 | ≥330 | 505 | ≥290 | 465 | ≥180 | 235 | ≥65 |
| 0.33° | 325 | ≥250 | 342 | ≥200 | 330 | ≥170 | 245 | ≥60 |
| 1° | 37 | ≥25 | 34.5 | ≥15 | 35 | ≥12 | 28 | ≥10 |
| 1°30′ | 19 | ≥10 | 18 | ≥7 | 16 | ≥5 | 19 | ≥4 |
Test Result of A001-1 Silver Reflective Tape
1.1 Abrasion
The test sample shall be abraded in accordance with EN 530:1994, method 2, using the woolen fabric abradant. The specimens shall be measured after 5 000 cycles and at a pressure of 9 KPa.
Retro-reflection after Abrasion
1.1 Abrasion
The test sample shall be abraded in accordance with EN 530:1994, method 2, using the woolen fabric abradant. The specimens shall be measured after 5 000 cycles and at a pressure of 9 KPa.
Retro-reflection after Abrasion
| Entrance Angle | Observation Angle | Measured value (cd/(lx )) | Minimum requirements (cd/(lx )) | Result |
| 5° | 0.2° | 380 | 100 | PASS |
1.2 Flexing
The test sample shall be flexed in accordance with EN ISO 7854:1997 method A. The specimens shall be measured after 7 500 cycles.
Retro-reflection after Flexing
The test sample shall be flexed in accordance with EN ISO 7854:1997 method A. The specimens shall be measured after 7 500 cycles.
Retro-reflection after Flexing
| Entrance Angle | Observation Angle | Measured value (cd/(lx )) | Minimum requirements (cd/(lx )) | Result |
| 5° | 0.2° | 373 | 100 | PASS |
1.3 Folding at cold temperatures
The test sample shall be exposed and folded in accordance with ISO 4675 at a temperature of (-20 ± 1)°C.
Measurements shall be made after reconditioning to the atmosphere for at least 2 h.
Retro-reflection after Folding at cold temperatures
| Entrance Angle | Observation Angle | Measured value (cd/(lx )) | Minimum requirements (cd/(lx )) | Result |
| 5° | 0.2° | 375 | 100 | PASS |
1.4 Exposure to temperature variation
Specimens of the size of 180 mm x 30 mm shall be exposed continuously to a cycle of changing temperatures:
a) for 12 h at (50 ± 2) °C immediately followed by
b) 20 h at (-30 ± 2) °C
c) Conditioning for at least 2 h in accordance with 7.1.
Retro-reflection after Temperature Variation
| Entrance Angle | Observation Angle | Measured value (cd/(lx )) | Minimum requirements (cd/(lx )) | Result |
| 5° | 0.2° | 398 | 100 | PASS |
1.5 Washing, Dry Cleaning
After 25 wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C.
| Entrance Angle | Observation Angle | Measured value (cd/(lx )) | Minimum requirements (cd/(lx )) | Result |
| 5° | 0.2° | 220 | 100 | PASS |
After 25 times washing, no Breakage, detachment, discoloration
After 5 times dry washing, no Breakage, detachment, discoloration
1.6 Retro-reflective performance in rainfall
Samples shall be tested in accordance with Annex D of this standard. Exposure at 284mm/h water flow for 2 hours. Retro-reflection after rainfall
After 5 times dry washing, no Breakage, detachment, discoloration
1.6 Retro-reflective performance in rainfall
Samples shall be tested in accordance with Annex D of this standard. Exposure at 284mm/h water flow for 2 hours. Retro-reflection after rainfall
| Entrance Angle | Observation Angle | Measured value (cd/(lx )) | Minimum requirements (cd/(lx )) | Result |
| 5° | 12' | 166 | 100 | PASS |