Measures to prevent stress corrosion cracking of welded joints of stainless steel storage tanks
In the production of stainless steel storage tanks, stress corrosion cracking of stainless steel welded joints is a relatively serious failure form of welded joints, which will affect the quality of equipment. The main preventive measures are:
(1) Reasonably formulate molding and assembly processes, minimize cold work deformation, avoid forced assembly, and prevent various scars during assembly.
(2) Appropriate welding processes are adopted in the production of stainless steel tanks to ensure that the welds are well formed without any stress concentration or pitting defects, such as undercuts, excessive weld heights, and pollution caused by splashes on the base metal.
(3) The production of stainless steel storage tanks adopts a reasonable welding sequence to reduce the level of welding residual stress.
How to avoid intergranular corrosion in stainless steel welding during the production of stainless steel storage tanks is a prerequisite for ensuring the welding quality and the overall quality of the equipment. Therefore, various preventive measures must be taken during welding.
This stainless steel jacke stoarge tank with jacket for cooling or heating;
The jacket type can be dimple pad or empty or coiled pipes, which can heat or cool the product inside;
Special design of flow path ensures the cooling or heating medium distribute much well in the jacket, so the heat exchange efficiency is high.
Use: Widely used for preparing(heating), sterilize, fermentation, aging, blending, cream storage etc.
1. Sus304 2B stainless steel
2. Dimple jacket or coil jacket for heating/cooling
3. Agitator 36rpm
Measures to prevent stress corrosion cracking of welded joints of stainless steel storage tanks
In the production of stainless steel storage tanks, stress corrosion cracking of stainless steel welded joints is a relatively serious failure form of welded joints, which will affect the quality of equipment. The main preventive measures are:
(1) Reasonably formulate molding and assembly processes, minimize cold work deformation, avoid forced assembly, and prevent various scars during assembly.
(2) Appropriate welding processes are adopted in the production of stainless steel tanks to ensure that the welds are well formed without any stress concentration or pitting defects, such as undercuts, excessive weld heights, and pollution caused by splashes on the base metal.
(3) The production of stainless steel storage tanks adopts a reasonable welding sequence to reduce the level of welding residual stress.
How to avoid intergranular corrosion in stainless steel welding during the production of stainless steel storage tanks is a prerequisite for ensuring the welding quality and the overall quality of the equipment. Therefore, various preventive measures must be taken during welding.
This stainless steel jacke stoarge tank with jacket for cooling or heating;
The jacket type can be dimple pad or empty or coiled pipes, which can heat or cool the product inside;
Special design of flow path ensures the cooling or heating medium distribute much well in the jacket, so the heat exchange efficiency is high.
Use: Widely used for preparing(heating), sterilize, fermentation, aging, blending, cream storage etc.
| Model | (L) Diameter | External diameter | Heightmm | Insulationδ | Jacketδ | Diameter of inlet/outlet |
| BYDG-500 | φ500 | 800 | 2140 | 50 | 1.5 | φ38 |
| BYDG-1 | φ1000 | 1050 | 2380 | 50 | 1.5 | φ38 |
| BYDG-1.5 | φ1500 | 1180 | 2550 | 50 | 1.5 | φ38 |
| BYDG-2 | φ2000 | 1340 | 2760 | 50 | 1.5 | φ38 |
| BYDG-2.5 | φ2500 | 1420 | 2940 | 50 | 1.5 | φ38 |
| BYDG-3 | φ3000 | 1540 | 3050 | 50 | 1.5 | φ38 |
| BYDG-4 | φ4000 | 1650 | 3200 | 50 | 1.5 | φ38 |
| BYDG-5 | φ5000 | 1780 | 3250 | 50 | 1.5 | φ38 |
| BYDG-6 | φ6000 | 1900 | 3350 | 50 | 1.5 | φ38 |
| BYDG-8 | φ8000 | 2100 | 3800 | 60 | 1.5 | φ65 |
| BYDG-10 | φ10000 | 2300 | 4050 | 60 | 1.5 | φ65 |
| BYDG-12 | φ12000 | 2520 | 4450 | 60 | 1.5 | φ65 |
Send Message